Felios Polyimide
Felios Polyimide
Flexible Polyimide Circuit Board Materials Suitable for Wide Range of Applications
R-F775 (Double-Sided)
R-F770 (Single-Sided)
Interested in Electronic Materials from Panasonic? Contact Us Now!
Resources
Part Number List
Results
2
Models table for series Felios Polyimide
Part No.
Datasheet
Tg (DSC) (°C)
Tg (TMA), (°C)
Tg (DMA) (°C)
Td (Thermal Decomposition) (°C)
T288 (Without Cu) (min)
T288 (With Cu) (min)
CTE-X, <Tg (ppm/℃)
CTE-Y <Tg (ppm/℃)
CTE-Z <Tg (ppm/℃)
CTE α2 Z-axis: Test Method IPC-TM-650 2.4.24; Condition A (ppm/℃)
Thermal Conductivity, (W/m・K)
Volume Resistivity (MΩ・cm)
Surface Resistivity (mΩ)
Dk at 1 GHz
Dk at 10 GHz
Dielectric Constant (Dk) @ 12Ghz; Test Method Balanced-type Circular Disk Resonator; Condition C-24/23/50
Df at 1 GHz
Df at 10 GHz
Df at 12 GHz
Water Absorption (%)
Flexural Warp (MD) (GPa)
Flexural Fill (TD) (GPa)
Peel Strength (1 Oz. Cu) (kN/m)
Flammability
Sample Thickness (mm)
R-F775
-
-
>340 (TPI 240)
577
-
-
18-20
16-19
-
-
0.16
-
-
3.2
3.2 Test method:Cavity resonance
3.1(19GHz)
0.002
0.004 Test method:Cavity resonance
0.003(19GHz)
0.9 Test method:Internal method
-
-
1.3(ED:18μm)
-
0.025mm
R-F770
-
-
>340 (TPI 240)
577
-
-
18-20
16-19
-
-
0.16
-
-
3.2
3.2 Test method:Cavity resonance
3.1(19GHz)
0.002
0.004 Test method:Cavity resonance
0.003(19GHz)
0.9 Test method:Internal method
-
-
1.3(ED:18μm)
-
0.025mm
Models table for series Felios Polyimide
Part No.
Datasheet
Tg (DSC) (°C)
Tg (TMA), (°C)
Tg (DMA) (°C)
Td (Thermal Decomposition) (°C)
T288 (Without Cu) (min)
T288 (With Cu) (min)
CTE-X, <Tg (ppm/℃)
CTE-Y <Tg (ppm/℃)
CTE-Z <Tg (ppm/℃)
CTE α2 Z-axis: Test Method IPC-TM-650 2.4.24; Condition A (ppm/℃)
Thermal Conductivity, (W/m・K)
Volume Resistivity (MΩ・cm)
Surface Resistivity (mΩ)
Dk at 1 GHz
Dk at 10 GHz
Dielectric Constant (Dk) @ 12Ghz; Test Method Balanced-type Circular Disk Resonator; Condition C-24/23/50
Df at 1 GHz
Df at 10 GHz
Df at 12 GHz
Water Absorption (%)
Flexural Warp (MD) (GPa)
Flexural Fill (TD) (GPa)
Peel Strength (1 Oz. Cu) (kN/m)
Flammability
Sample Thickness (mm)
R-F775
-
-
>340 (TPI 240)
577
-
-
18-20
16-19
-
-
0.16
-
-
3.2
3.2 Test method:Cavity resonance
3.1(19GHz)
0.002
0.004 Test method:Cavity resonance
0.003(19GHz)
0.9 Test method:Internal method
-
-
1.3(ED:18μm)
-
0.025mm
R-F770
-
-
>340 (TPI 240)
577
-
-
18-20
16-19
-
-
0.16
-
-
3.2
3.2 Test method:Cavity resonance
3.1(19GHz)
0.002
0.004 Test method:Cavity resonance
0.003(19GHz)
0.9 Test method:Internal method
-
-
1.3(ED:18μm)
-
0.025mm
What's New
Stay up to date
View All
Panasonic Circuit Board Materials Featuring MEGTRON and More!
Electronic Materials Icon
Panasonic Circuit Board Materials Featuring MEGTRON and More!
Introducing the Electronic Materials Product Line
Electronic Materials Icon
Introducing the Electronic Materials Product Line
Panasonic RUGGED RANTS Podcast Answers What Are E-Textiles!
Electronic Materials Icon
Panasonic RUGGED RANTS Podcast Answers What Are E-Textiles!
Navigate Previous
Navigate Next