| Tg (TMA) (⁰C ) | 218 |
| CTE-1 (TMA) (ppm/℃) | 9 |
| Flexural Modulus (@25⁰C) (GPa) | 10 |
| Filler Size (Max) (μm) | 20 |
| Mold Shrinkage (%) | 0.11 |
| Filler Type (FusedSilica/CrystalineSilica/Alumina) | Fused |
| Filler Shape (Spherical/Flake) | Spherical |
| Filler Content (in Ash) (% wt) | 82 |
| Filler size (Avg) (μm) | 5 |
| Sprial Flow (cm) | 181 |
| Gelation Time (Sec) | 59 |
| Viscosity (@175⁰C) (Pa Sec) | 15 |
| Specific gravity | 1.90 |
| CTE-2 (TMA) (ppm/℃) | 50 |
| Flexural Strength(@25⁰C) (MPa) | 50 |
| Flexural Strength(@260⁰C) (MPa) | 7 |
| Flexural Modulus(@260⁰C) (GPa) | 0.5 |
| Dielectric Constant (1MHz) | 4.1 |
| Dissipation Factor (1MHz) | 0.017 |
| Flame Retardant (Yes/No) | No |
| Flammability (UL-94) | HB |
| Thermal Conductivity (W/mK) | 0.8 |
| Low Alpha Type (Yes/No) | No |