R-F705S (Double-sided)
Specification
| Item | Performance characteristics |
|---|---|
| Tg (DSC) (°C) | - |
| Tg (TMA), (°C) | - |
| Tg (DMA) (°C) | - |
| Td (Thermal Decomposition) (°C) | - |
| T288 (Without Cu) (min) | - |
| T288 (With Cu) (min) | - |
| CTE-X, <Tg (ppm/℃) | 17-19 |
| CTE-Y <Tg (ppm/℃) | 17-19 |
| CTE-Z <Tg (ppm/℃) | - |
| CTE α2 Z-axis: Test Method IPC-TM-650 2.4.24; Condition A (ppm/℃) | - |
| Thermal Conductivity, (W/m・K) | - |
| Volume Resistivity (MΩ・cm) | - |
| Surface Resistivity (mΩ) | - |
| Dk at 1 GHz | - |
| Dk at 10 GHz | 3.3 Test method: Cavity resonance |
| Dielectric Constant (Dk) @ 12Ghz; Test Method Balanced-type Circular Disk Resonator; Condition C-24/23/50 | 2.9(19GHz) |
| Df at 1 GHz | - |
| Df at 10 GHz | 0.002 Test method: Cavity resonance |
| Df at 12 GHz | 0.002(19GHz) |
| Water Absorption (%) | 0.04 Test method: Internal method |
| Flexural Warp (MD) (GPa) | - |
| Flexural Fill (TD) (GPa) | - |
| Peel Strength (1 Oz. Cu) (kN/m) | 1.0(ED:18μｍ) |
| Flammability | - |
| Sample Thickness (mm) | 0.05ｍｍ |
Stock Check
Important
The service is owned, operated, controlled and managed by Panasonic's distributors.
For pricing, delivery and technical questions related to this service, please direct to them.
Panasonic assumes no responsibility for any dealings you may have with distributors.
What's New
Stay up to date
Latest Videos
Playlist
Electronic Materials
MEGTRON and XPEDION Series: Connecting to the Future with PCB Materials
Electronic Materials Icon